Characterizing the Brittle Fracture and the Ductile to Brittle to Ductile Transition of Heat-Treated Binary Aluminum-Lithium Alloys

J.M. Fragomeni
Ohio University
United States

An aluminum alloy containing 2.6wt.% Li and 0.09wt.% Zr exhibited a very low value in tensile ductility consistently prior to the peakaged strength independent of thermal treatment. A transition was characterized by very low ductility in the slightly underaged condition up to the near peakaged condition, then followed by a substantial increase in ductility with aging after the peakaged treatment. In order to better understand the deformation and fracture, a scanning electron microscopy study of the fracture surfaces of Al-2.6wt.% Li-0.09wt.% Zr tensile samples solution heat-treated and artificially aged was performed to relate the mechanical behavior to microstructure in the precipitation hardened Al-Li alloy. SEM analysis of the surface features and fracture morphology of the alloy was performed to understand the mechanisms of fracture in relation to the ductile-to-brittle transition that resulted in the alloy from precipitation hardening. TEM analysis was also performed to characterize the deformation behavior, and revealed the distribution of precipitates (both Al$_3$Li ($\delta^\prime$) and Al$_3$Zr-Al$_3$Li) in the microstructure at very high magnifications as well as the dislocation subgrain structure of the alloy at lower magnification. It follows from this study that the presence of $\delta^\prime$ particles in the matrix promotes intense planar slip which was believed to be responsible for the ultra-low ductility prior to the peakaged temper. Based on a detailed quantitative microscopy study, it was proposed that the increase in the ductility of the alloy after aging was a consequence of particle coarsening with aging thus resulting the Orowan process due to the transition from dislocation particle shearing to dislocation particle bypassing.
Full Text: PDF
Copyright © Polish Academy of Sciences & Institute of Fundamental Technological Research (IPPT PAN).


T. H. SANDERS Jr., Factors affecting toughness and other properties of aluminium-lithium alloys, final report, Naval Air Development Center, N62269–76–C–0271, 1976.

E.A. STARKE Jr., The application of the fundamentals of strengthening to the design of new aluminum alloys, Proceedings of the 6th International Conference on the Strength of Metals and Alloys (ICSMA 6), pp. 1025–1044, Melbourne, 1982.

K. WELPMANN, M. PETERS and T.H. SANDERS Jr., Aluminum-lithium alloys, Aluminum, 60, 10, pp. E641–646, 11, pp. E709–712, 1984.

1988 Annual book of ASTM standards, section 3: metals test methods and analytical procedures, Volume 3.01, American Society for Testing and Materials, Philadelphia, PA, 1988.

B.P. Gu, G.L. JHA, G.L. LIELD, K. MAHALINGAM and T.H. SANDERS Jr., Microstructure and the behavior of aluminium-lithium alloys, Light Metals, Materials Research Society, 35–43, 1985.

S. SURESH, A.K. VASUDEVAN, M. TOSTEN and P. R. HOWELL, Microscopic and macroscopic aspects of fracture in lithium-containing aluminum alloys, Acta Metallurgica, 35, 1, 25–46, 1987.

E. OROWAN, Symposium on internal stresses in metals and alloys, session III discussion, Institute of Metals, p. 451, London 1948.

B. NOBLE, S.J. HARRIS and K. DINSDALE, The elastic modulus of aluminium-lithium alloys, Metal Science, 16, 425–430, 1982.

E.J. LAVERNIA and N.J. GRANT, Review aluminium-lithium alloys, Journal of Material Science, 12, 1521–1529, 1987.

P.J. GREGSON and H.M. FLOWER, Micro structural control of toughness in aluminium-lithium alloys, Acta Metallurgica, 32, 2, 527–537, 1985.

E.A. STARKE Jr., T.H. SANDERS Jr. and I.G. PALMER, New approaches to alloy development in the Al–Li system, the effect of slip on the monotonic and cyclic ductility of Al-Li binary alloys, Journal of Metals, 33, 8, 24–33, 1981.

T.H. SANDERS JR. and E A. STARKE Jr., The effect of slip distribution on the monotonic and cyclic ductility of Al-Li binary alloys, Acta Metallurgica, 30, 927–939, 1982.

B. P. Gu, S.C. JHA, G. L. LEIDL, K. MAHALINGHAM and T.H. SANDERS Jr., Microstructure and the behavior of aluminumlithium alloys, proceedings of the European Materials Research Society, Advanced Materials Research and Development for Transport, 1985.

E.A. STARKE Jr., and G. LUTJERING, Cyclic plastic deformation and micro structure, fatigue and micro structure, M. MESHI [Ed.], American Society for Metals, Metals Park, 205–213, Ohio 1979.

M. MEURIS and E. HORNBOGEN, Localized slip and intergranular fracture in age-hardening aluminum alloys, Pract. Metallogr., 13, 4, 160–171, 1976.

T. H. SANDERS Jr., Al-Li-X alloys – an overview, aluminium-lithium alloys, T.H. SANDERS, Jr. and E. A. STARKE Jr. [Eds.], The Metallurgical Society of AIME, 63–67, 1980.

E.I. MELETIS, J.M. SATER and T.H. SANDERS Jr., Environmental assisted cracking in aluminium-lithium alloys, aluminum alloys: their physical and mechanical properties, vol. II, E. A. STARKE Jr. and T. H. SANDERS Jr. [Eds.], Engineering Materials Advisory Services, 1157–1175, United Kingdom 1986.

A.W. THOMPSON, Modeling of Local strains in ductile fracture, Metallurgical Transactions A., ISA, 1877–1886, 1987.

A.K. VASUDEVAN, E.A. LUDWICZAK, P.R. BAUMANN, P.R. HOWELL, R.D. DOHERTY and M. M. KERSKER Aluminum-lithium alloys III, C. BAKER, P. J. GREGSON, S. J. HARRIS and C. J. PEEL [Eds.], The Institute of Metals, 490–495, London 1986.

A.K. VASUDEVAN, E.A. LUDWICZAK, B.F. BAUMAN, R.D. DOHERTY and M.M. KERSKER Fracture behavior in Al-Li alloys, Material Science and Engineering, 72, L25–L30, 1985.

P. SAINFORT and P. GUYOT, Fundamental aspects of hardening in Al-Li and Al-L-Cu Alloys, Aluminum-Lithium Alloys HI, C. BAKER, P.J. GREGSON, S.J. HARRISON, and C.J. PEEL [Eds.], The Institute of Metals, 420–426, London 1986.

A. K. VASUDEVAN and S. SURESH, Micro structural effects on quasi-static fracture mechanisms in Al-Li alloys: the role of crack geometry, Material Science and Engineering, 72, 37–49, 1985.

A.K. VASUDEVAN and R.D. DOHERTY, Grain boundary ductile fracture in precipitation hardened aluminum alloys, Acta Metallurgica, 35, 6, 1193–1219, 1987.

G.G. GARRETT and J.F. KNOTT, The influence of compositional and micro structural variations on the mechanism of static fracture in aluminum alloys, Metallurgical Transactions A, 9A, 1187–1201, 1978.

D.W PASHLEY, M.H. JACOBS and J.T. VIETZ, The basic processes affecting two–step ageing in an Al-Mg-Si alloy, Philosophical Magazine, 16, 51–57, 1967.

T.H. SANDERS Jr., E.A. LUDWICZAK and R.R. SAWTELL, The fracture behavior of recrystallized Al-2.8wt.% Li-0.3wt.% Mn sheet, Materials Science and Engineering, 43, 247–260, 1980.

F.S. LIN, S.B. CHAKRABORTTY and E.A. STARKE Jr., Micro structure–property relationships of two Al3-Li2-Cu0.2-Zr alloys, Metallurgical Transactions A, 13a, 401–410, 1982.

M. FURUKAWA, Y. MIURA and M. NEMOTO, Strengthening mechanisms in Al-Li alloys containing ordered particles, Transactions of the Japan Institute of Metals, 26, 4, 230–235, 1985.

A. PINEAU, F. LECROISEY, J.L. CASTAGNE, M. SINDZINGRE, Yielding of an alloy hardened by coherent and ordered precipitation, Acta Metallurgica, 17, 905, 1969.

J. LIVINGSTON, Critical particle size for precipitation hardening, Transactions of the Metallurgical Society of AIME, 215, 55–59, 1959.

I.M. LIFSHITZ and V.V. SLYOZOV, The kinetics of precipitation from supersaturated solid solutions, Journal Physical Chemical Solids, 19, 35–50, 1961.

C. WAGNER, Theories associated with age hardening and Overaging during Ostwald ripening [in German], Zeitschrift für Elekrochemie, 3, 7, 581–591, 1961.

J.M. DUVA, M.A. DAEUBLER, E.A. STARKE Jr. and G. LUETJERING, Acta Metallurgica, 36, 585, 1988.

DOI: 10.24423/engtrans.543.2001